Archive

Aviation materials and tecnologes №4, 2011

UDC: 620.197

S.S. Solntsev, V.A. Rosenenkova, N.A. Mironova, S.V. Gavrilov

Ceramic coatings for the protection of high-strength steels during the heat treatment

The versatile frit-free coatings have been developed for the protection of high-strength steels of VKS type against the oxidation and burning out of alloying elements during the high-temperature heat treatment. The oxidation kinetics of ВКС steels with and without coatings was strudied during the full cycle of heat treatment. The application efficiency of frit-free coatings is shown for ВКС steels.

Keywords: ceramic frit-free coatings, oxidability, high-strength steels

Reference List

  1. Солнцев С.С. Защитные технологические покрытия и тугоплавкие эмали. М.: Машиностроение. 1984. С. 113-139.
  2. Солнцев С.С., Розененкова В.А., Исаева Н.В., Швагирева В.В. Применение стеклокерамических материалов и покрытий в авиакосмической технике //Авиационные материалы. Избранные труды «ВИАМ» 1932-2002 Юбилейный научно-технический сборник. М.: МИСиС-ВИАМ. 2002. С. 137-150.

UDC: 621.775.8:66.045.3

D.V. Graschenkov, B.V. Schetanov, E.V Tinyakova, T.M. Scheglova

Possible application of quartz fiber as a binder when producing a light-weight thermoprotective material on the base of fiber Al2O3

The formation mechanism of fibrous three-dimensional (3D) frame structure of Al2O3-base fibers with the use of quartz fibers as a binder is considered in the present paper.

Keywords: thermoprotective material, thermoinsulation material, fiber, aluminium oxide, guartz, binder, diffusion, heat treatment

Reference List

  1. www.saffil.com, www.dyson-group.com.
  2. www.3m.com
  3. www.boeing.com
  4. www.zircarceramics.com
  5. www.unifrax.com
  6. www.aerospatiale.com
  7. www.yes-mpi.com
  8. Щетанов Б.В., Каблов Е.Н., Щеглова Т.М. Механизм формирования стабилизированной структуры в высокотермостойких поликристаллических волокнах системы Al2O3-SiO2, получаемых по золь-гель технологии: Материалы 24-й ежегодной междунар. конф. «Композиционные материалы в промышленности». Ялта. 2004. С. 324-326.
  9. Refractory fibrous ceramic unsulation and process of making same: пат. 6183852 США; опубл. 06.02.2011.
  10. Ceramic insulation: пат. 6417125 США; опубл. 09.07.2002.
  11. Способ получения волокнистой заготовки металлокомпозита: заявка на изобретение RU 94008408 Рос. Федерация; заявл. 09.03.94; опубл. 27.11.95.
  12. Павлушин Н.М. Основы технологии ситаллов. М.: Изд-во лит. по строительству. 1970. С. 36.
  13. Бережной А.И. Ситаллы и фотоситаллы. 2-е изд., перераб. и доп. М.: Машиностроение. 1981. 464 с.
  14. Wen-Cheng W., Halloran J.W. Transformation Kinetics of Diphase Alumina-Silicate Gels //J. Am. Ceram. Soc. 1988. V. 71(7). Р. 581-587.

UDC: 621.039.546

A.V. Panarin

Pyrolytic chromium carbide coatings. Production technology and properties

The method of producing the coatings out of vapour phase is described by the way of organometallic compound decomposition. The production technological particularities of pyrolytic chromium carbide coating out of organochromium liquid were strudied with the use of ВРПО-16 unit; the basic physical, chemical and service properties of the produced coating were also examined.

Keywords: pyrolytic coating, organochromium liquid, organometallic compound, chromium carbide

Reference List

  1. Защитное пиролитическое хромовое покрытие. Технология, свойства, применение: Обзор В.Ф. Соколова и др. М.: ЦНИИатоминформ. 1989. С. 3.
  2. А/С СССР № 598964 В.А. Костенков и др. Способ осаждения покрытий из паровой фазы. 1978.
  3. А/С СССР № 638664 А.С. Лузин и др. Способ нанесения хромкарбидного покрытия. 1978.
  4. Ильин В.А. Разработка и исследование технологических режимов осаждения износостойких и коррозионностойких пиролитических карбидохромовых покрытий на материалы изделий авиационной техники: Диссертация на соискание ученой степени к. т. н. М. 2002. С. 56.

UDC: 678.8

S.V. Strelnikov, O.B. Zastrogina, E.A. Veshkin, N.I. Shvets

Development of highly effective technologies for the commercial production of interior panels

The analysis of the technological effectiveness of existing passenger aeroplane interiors was made along with determining the basic trends of its improvement applied to the commercial production as well as the panel moulding priorities according to the combined technology by the adhesive-free method with the use of prepregs, polymer fillers and hot-cured gel coats on the base of high-concentrated binders of ФПР-520, ФПР-520G and ПС-Н types. The maximum use of bended panels and tenon joints in life block structures is the reserve of reducing the nomenclature of applied parts and the product weight reduction.

Keywords: passenger aeroplane interior, interior panels, prepreg, polymer filler, gel coat

Reference List

  1. Постнов В.И., Петухов В.И. Технологическое совершенствование процессов изготовления панелей интерьера самолетов //Известия Самарского науч. центра РАН. Спец. выпуск Т. 1. 2008. С. 65-70.
  2. Крысин В.Н., Крысин М.В. Технологические процессы формования, намотки и склеивания конструкций. М.: Машиностроение. 1989. 240 с.
  3. Кирин К.М. Перспективные пожаробезопасные текстильные материалы для применения в гражданской авиации: Автореф. диссертации на соискание ученой степени канд. техн. наук. М: ГОУ ВПО РосЗИТЛП. 2004. 16 с.
  4. Минаков В.Т., Постнов В.И., Швец Н.И., Застрогина О.Б., Петухов В.И., Макрушин К.В. Особенности изготовления трехслойных сотовых панелей с полимерным заполнителем горячего отверждения //Авиационные материалы и технологии. 2009. № 3. С. 6-9.

UDC: 669.24:669.018.44:66.065.5

E.N. Kablov, Yu.A Bondarenko, D.E. Kablov

Particularities of <001> single crystals structure and heat-resistant properties of high-rhenium Ni-base superalloy, produced under the high-gradient directed solidification conditions

The effect of the directed solidification with the high-temperature gradient on the growth front upon the structure, dendrite liquation, porosity and heat resistance of the present-day rhenium-containing superalloy with <001> single-crystal structure, being developed for GTE blade casting was under investigation.

Keywords: high gradient directed solidification, superalloys, single-crystal structure, dendrite liquation, porosity, stress rupture, fatigue

Reference List

  1. Каблов Е.Н., Светлов И.Л., Петрушин Н.В. Никелевые жаропрочные сплавы для литья лопаток с направленной и монокристаллической структурой //Материаловедение. 1997. № 4. с. 32?38. № 5. С. 14-17.
  2. Каблов Е.Н, Бондаренко Ю.А. Новое в технологии производства лопаток ГТД //Аэрокосмический курьер. 1999. № 2. С. 60-62.
  3. Бондаренко Ю.А., Каблов Е.Н. Направленная кристаллизация жаропрочных сплавов с повышенным температурным градиентом //МиТОМ. 2002. № 7. С. 20-23.
  4. Бондаренко Ю.А., Каблов Е.Н., Морозова Г.И. Влияние высокоградиентной направленной кристаллизации на структуру и фазовый состав жаропрочного сплава типа Rene N5 //МиТОМ. 1999. № 2. С. 15-18.

UDC: 678.7

Yu.V. Sytyi, V.I. Kislyakova, V.A. Sagomonova, M.F. Nikolaeva

New ВТП-2П multilayer sealant

The basic service properties of ВТП-2П multilayer sealant were considered in the initial state and after the environmental factors effect. The ВТП-2П multilayer sealant is recommended for sealing the layers of pneumo-, hydro- and fuel systems, operating in the temperature range from -60 to +260°C, which will allow to increase the reliability and service life of the aggregate sealings.

Keywords: multilayer sealant, pneumosystems, hydraulic systems, fuel systems, teflon, compression, creep, residual deformation, fluoroplastic-4

Reference List

  1. Паншин Ю.А., Малкевич С.Г., Дунаевская Ц.С. Фторопласты //Химия. 1978. С. 49-53.
  2. Пугачев А.К., Росляков О.А. Переработка фторопласта в изделия //Химия. 1987. С. 46-51.

UDC: 620.178.35

V.S. Erasov, G.A. Nuzhnyi

Rigid loading cycle in studies of fatigue failure

The danger of the fatigue failure, its propogation mechanism and diagnostics difficulties of such failure are described along with the features of fatigue tests, mainly the tests under the rigid cyclic loading conditions and its perspective application.

Keywords: rigid cyclic loading, fatigue tests, mechanical hysteresis loop

Reference List

  1. Терентьев В.Ф. Усталость металлических материалов. М.: Наука. 2003. 254 с.
  2. Терентьев В.Ф. Полная кривая усталости металлов и сплавов //Технология металлов. 2004. №6. С. 12-16.
  3. Степнов М.Н., Чернышев С.Л., Ковалев И.Е., Зинин А.В. Характеристики сопротивления усталости. Расчетные методы оценки. М.: Технология машиностроения. 2010. 256 с.

UDC: 620.1

V.N. Kirillov, V.A. Efimow, A.K. Shvedkova, E.V. Nikolaev

Testing of climatic factors and the mechanical loading effect upon the polymer composite structure and properties

The test results, aimed at studying КМУ-11тр carbon fiber reinforced plastics moisture absorption kinetics, the absorbed moisture effect upon the glass-transition temperature range and bending strength in the process of accelerated (heat and moisture) and full-scale researches are given in the present paper. The specimen bending loading was found to be capable of increasing the homogeneity of polymer matrix structure.
It was also reveled, that the binder glass transition temperature was decreased at the moment of increasing the specimen loading.

Keywords: polymer composites, environmental factors, strength, moisture absorption, glass transition temperature

Reference List

  1. Болотин В.В. Прогнозирование ресурса машин и конструкций. М.: Машиностроение. 1984. 312 с.
  2. Вапиров Ю.М., Кириллов В.Н., Кривонос В.В. Закономерности изменения свойств полимерных композитов конструкционного назначения при длительном климатическом старении в свободном и нагруженном состояниях //В сб. докладов VI научной конференции по гидроавиации «Гидроавиасалон-2006». М. 2006. Ч. II. С. 103-108.
  3. Старцев О.В. Старение полимерных авиационных материалов в теплом влажном климате: Автореф. дис. д-ра техн. наук. М. 1990. 80 с.
  4. Панферов К.В., Романенков И.Г., Абашидзе Г.С., Никитин В.Н., Львов Б.С., Шпаловская Б.И. Атмосферостойкость стеклопластиков, находящихся под нагрузкой //Пластмассы. 1968. №6. С. 32-33.
  5. Булманис В.Н., Ярцев В.А., Кривонос В.В. Работоспособность конструкций из полимерных композитов при воздействии статических нагрузок и климатических факторов //МКМ. 1987. №5. С. 915-920.
  6. Кириллов В.Н., Ефимов В.А., Матвеенкова Т.Е., Коренькова Т.Г. Влияние последовательного воздействия климатических и эксплуатационных факторов на свойства полимерных композиционных материалов //В сб. докладов V научной конференции по гидроавиации «Гидроавиасалон-2004». М. 2004. С. 155-158.
  7. Кириллов В.Н., Ефимов В.А., Вапиров Ю.М. Особенности влияния внешних факторов на свойства ПКМ при ускоренных и натурных климатических испытаниях //В сб. докладов VII научной конференции по гидроавиации «Гидроавиасалон-2008». М. 2008. Ч. 1. С. 327-335.